Cyclic Oxidation of High Temperature Materials EFC 27: Mechanisms, Testing Methods, Characterisation and Life Time Estimation - Proceedings of an EFC Workshop

by Schutze; Michael

• ISBN13: 9781861251008
• ISBN10: 1861251009
• eBook ISBN(s): 9781040282281
• Format: Hardcover
• Copyright: 1999-08-01
• Publisher: CRC Press

Summary

Proceedings of a workshop organised by the European Federation of Corrosion, Frankfurt/Main, 1999, the papers review the current understanding of materials behaviour under cyclic oxidation.

Table of Contents

Series Introduction
Preface
Foreword
Interfacial Crack Growth During Temperature Changes	p. 3
The Influence of Surface Pre-treatment on the Integrity of Alumina Scales on the ODS Alloy MA 956	p. 17
The Effect of Water Vapour on the Oxidation of Alloys that Develop Alumina Scales for Protection	p. 38
The Influence of Thermal Cycling on Internal Oxidation and Nitridation of Nickel-Base Alloys	p. 63
Cyclic Oxidation of Thin FeCrAl(RE) Foils in Air: SEM and EPMA Investigations	p. 82
Cyclic Oxidation of PM 1000	p. 95
Effect of Cycle Frequency on High-Temperature Oxidation Behaviour of Alumina- and Chromia-Forming Alloys	p. 111
The Effect of Thermal Cycling on the Mechanical Failure of Alumina Scales formed on Commercial FeCrAl-RE Alloys	p. 133
Cyclic Oxidation Testing and Modelling: a NASA Lewis Perspective	p. 148
Significance of Experimental Procedures on the Hot Corrosion Behaviour of Nickel-Base Alloys under Cyclic Conditions	p. 169
Advantages of Ferritic Stainless Steels in Cyclic High Temperature Conditions	p. 187
Investigation of a New Methodology in High Temperature Oxidation	p. 198
Effect of Implanted Silicon on the Cyclic Oxidation Behaviour of AISI 304 and AISI 430 Stainless Steels	p. 209
The Importance of Relevant Experimental Parameters for High Temperature Cyclic Oxidation Experiments - An attempt for a checklist	p. 225
Corrosion of Heat Exchanger Steels in Cycled Gas Atmospheres at 600[degree]C	p. 240
Behaviour of Protective Coatings against Sulfidation under Cyclic Conditions	p. 259
Long-Term, Cyclic Oxidation Behaviour of Three Chromia-Forming Alloys Exposed to Air at 982[degree]C	p. 273
Oxidation Limited Life of FeCrAl Based Alloys During Thermal Cycling	p. 287
Characterisation of Oxidation Resistance of Heat-resistant Cast Alloys in the 5 x 24-h Test	p. 307
Cyclic Oxidation Testing by Resistance Heating	p. 324
Thermal Cycling Testing of Thermal Barrier Coatings	p. 339
Investigations of the Microstructure and Stress State in Oxide Scales and Buried Layers with Diffraction Methods	p. 357
Numerically Calculated Oxidation Induced Stresses in Thermal Barrier Coatings on Cylindrical Substrates	p. 373
Electron Beam - Physical Vapour Deposited Thermal Barrier Coating Lifetime Response to Various Bond Coat Pre-treatments	p. 383
Degradation of Aluminide, Chromium - Aluminide and Thermal Barrier Coatings in Conditions of Cyclic Thermal and Mechanical Loads	p. 392
Thermal Cycling of NiAl Intermetallic Coatings Prepared by High Velocity Oxy-Fuel (HVOF) Thermal Spraying	p. 408
Development of Metal - Organic Chemical Vapour Deposition (MOCVD) Coatings for Protection of Alloys under High Temperature Cyclic Conditions	p. 421
Mullite Based Oxidation Protection for Silicon Carbide - Carbon/Carbon Composites in Air at Temperatures up to 1900K	p. 431
Cyclic Oxidation - Guidelines for Test Standardisation, Aimed at the Assessment of Service Behaviour	p. 437
List of Abbreviations	p. 471
Index	p. 473